Epoxies & Protective Coating
MC-Poly Paint T.C
Two Component Polyurethane Coating
MC-Poly Paint T.C is a two- pack polyurethane top coat.
| Colour | Clear and available in a wide range of colours |
|---|---|
| Specific gravity @ 25°C - coloured | 1.40 ± 0.05 after mixing |
| Solids by volume | 70% ± 2 |
| Gloss | Glossy |
| Flexibility | Good |
| Recommended dry-film thickness | 50 µm |
| Application method | Airless spray, brush or roller |
| Pot life @ 20°C | 6 hours; reduced at higher temperature |
| Thinner / cleaner | MC-Thinner 03 |
| Airless spray pressure | 1500-1800 psi at nozzle |
| Nozzle tip | 0.013-0.018 in |
| Spray angle | 30°-75° |
| Coloured | 4.5 kg A + 0.5 kg B - A:B = 9:1 |
|---|---|
| Clear | 3 kg A + 1 kg B - A:B = 3:1 |
Description
MC-Poly Paint T.C is a two-pack polyurethane top coat.
Where to use
Top coat over MCT epoxy systems where protection against aggressive atmospheric conditions is required. Protection of surfaces exposed to severe weather and direct sunlight.
Advantages
Durable. Very good gloss retention. Excellent UV resistance. Good flexibility. Excellent adhesive properties on steel, wood, concrete, asbestos, PVC and polypropylene according to the approved source.
Drying time
Substrate Surface dry Cured Minimum recoat 10°C 8 hours 17 days 24 hours 25°C 7 hours 5 days 18 hours 35°C 6 hours 4 days 16 hours
Application conditions
The surface must be clean, dry and free from contamination. During application, substrate temperature should be at least 10°C and at least 3°C above the air dew point.
Mixing & packaging
Coloured 4.5 kg A + 0.5 kg B - A:B = 9:1 Clear 3 kg A + 1 kg B - A:B = 3:1
Storage
Keep containers tightly closed in a suitable dry place. Stir components thoroughly before use according to the technical source.